Grade C sucker rod is made from fine carbon steel. It is featured by mid-strength, good plasticity, toughness, corrosion resistance. It is suitable for sour medium environment where it is not susceptible to sulphuric stress cracking.
Grade D sucker rod is made from fine alloy steel, featured by high strength, better plasticity and long service life after heat treatment. This product is suitable for no-corrosion or light-corrosion environment oil-well widely.
Grade HL and HY sucker rods are super-high strength sucker rod, having the same size and main parameter as grade D sucker rod, but their strength is capable to reach 966~1195Mpa. Grade HL, HY sucker rods are suitable for the deep oil-well or big-pump capacity oil-well.
And grade K, KD and KH sucker rod are made from fine Cr-Ni-Mo alloy steel containing different amount of Ni. They possess more powerful anti-corrosion function. The products are suitable for strong corrosion oil-well, with depth of shallow, middle and deep respectively.
.
Mechanical Properties Of Steel Sucker Rod:
| Sucker Rod Weight List | |||||||
| Size | 5/8" | 3/4" | 7/8" | 1" | 1-1/8" | 1-1/4" | 1-1/2" |
| kg/m | 1.68 | 2.4 | 3.2 | 4.2 | 5.3 | 6.4 | 9.5 |
| Mechanical Property OF Steel Polished Rod | |||||||||||
| GRADE | Minimum Yield Strength(0.2% Residual Deformation) | Minimum Tensile Strength | Maxmum Tensile Strength | Elongation200mm% | Reduction of Area Z% | HRC | HB | Fatigue Life | |||
| psi | MPa | psi | MPa | psi | MPa | ≥13 | ≥50 | ≥1.0X106 | |||
| C | 60000 | 414 | 90000 | 621 | 115000 | 793 | ≥13 | ≥50 | |||
| D | 85000 | 586 | 115000 | 793 | 140000 | 965 | ≥13 | ≥50 | |||
| KD | 85000 | 590 | 115000 | 795 | 140000 | 965 | ≥13 | ≥50 | |||
| H | 115000 | 795 | 140000 | 965 | 173339 | 1195 | ≥13 | ≥45 | |||
| EHL | / | / | 188500 | 1300 | 217500 | 1500 | / | / | ≥50 | ≥320 | ≥2.5X106 |
| Note: When the minimum yield strength cannot be measured, it should be considered to be processed into standard sample and install extensometer to measure. | |||||||||||
| a It is generally made of high quality carbon steel, which can reach the mechanical properties of the table b A molybdenum steel (but not limited to this type of steel) is generally used, and the effective heat treatment can achieve the mechanical properties of this table |
|||||||||||
| SN | Normal size in(mm) | Dia. of coated rod (mm) | Wrench section width (mm) | Wrench section Length (mm) | OD of Male thread step (mm) | Nipple neck length of ascension(mm) |
| 1 | 5/8(16) | 19 | 27 | 28 | 37 | 127 |
| 2 | 3/4(19) | 22 | 29 | 28 | 43 | 127 |
| 3 | 7/8(22) | 25 | 29 | 28 | 45 | 127 |
| 4 | 1(25) | 28 | 39 | 28 | 55 | 127 |
| 5 | 1 1/8(29) | 32 | 43 | 37 | 60 | 127 |
Lake Petro is located in Dongying City, which is famous for Shengli Oilfield and the largest manufacturing hub of petroleum equipment in China. Following the principle of "quality first, science and technology innovated, people oriented", every Lake Petro person is sparing no effort to provide the customers with best products and services. Our products are based on advanced production line and testing equipment, our products are designed and manufactured according to certification of ISO, GOST, etc.
How can I place order?
A: You can contact us by email about your order details, or place order on line.
){kind=link}